Accendo Reliability

Your Reliability Engineering Professional Development Site

  • Home
  • About
    • Contributors
  • Reliability.fm
    • Speaking Of Reliability
    • Rooted in Reliability: The Plant Performance Podcast
    • Quality during Design
    • Way of the Quality Warrior
    • Critical Talks
    • Dare to Know
    • Maintenance Disrupted
    • Metal Conversations
    • The Leadership Connection
    • Practical Reliability Podcast
    • Reliability Matters
    • Reliability it Matters
    • Maintenance Mavericks Podcast
    • Women in Maintenance
    • Accendo Reliability Webinar Series
  • Articles
    • CRE Preparation Notes
    • on Leadership & Career
      • Advanced Engineering Culture
      • Engineering Leadership
      • Managing in the 2000s
      • Product Development and Process Improvement
    • on Maintenance Reliability
      • Aasan Asset Management
      • AI & Predictive Maintenance
      • Asset Management in the Mining Industry
      • CMMS and Reliability
      • Conscious Asset
      • EAM & CMMS
      • Everyday RCM
      • History of Maintenance Management
      • Life Cycle Asset Management
      • Maintenance and Reliability
      • Maintenance Management
      • Plant Maintenance
      • Process Plant Reliability Engineering
      • ReliabilityXperience
      • RCM Blitz®
      • Rob’s Reliability Project
      • The Intelligent Transformer Blog
      • The People Side of Maintenance
      • The Reliability Mindset
    • on Product Reliability
      • Accelerated Reliability
      • Achieving the Benefits of Reliability
      • Apex Ridge
      • Metals Engineering and Product Reliability
      • Musings on Reliability and Maintenance Topics
      • Product Validation
      • Reliability Engineering Insights
      • Reliability in Emerging Technology
    • on Risk & Safety
      • CERM® Risk Insights
      • Equipment Risk and Reliability in Downhole Applications
      • Operational Risk Process Safety
    • on Systems Thinking
      • Communicating with FINESSE
      • The RCA
    • on Tools & Techniques
      • Big Data & Analytics
      • Experimental Design for NPD
      • Innovative Thinking in Reliability and Durability
      • Inside and Beyond HALT
      • Inside FMEA
      • Integral Concepts
      • Learning from Failures
      • Progress in Field Reliability?
      • R for Engineering
      • Reliability Engineering Using Python
      • Reliability Reflections
      • Testing 1 2 3
      • The Manufacturing Academy
  • eBooks
  • Resources
    • Accendo Authors
    • FMEA Resources
    • Feed Forward Publications
    • Openings
    • Books
    • Webinars
    • Journals
    • Higher Education
    • Podcasts
  • Courses
    • 14 Ways to Acquire Reliability Engineering Knowledge
    • Reliability Analysis Methods online course
    • Measurement System Assessment
    • SPC-Process Capability Course
    • Design of Experiments
    • Foundations of RCM online course
    • Quality during Design Journey
    • Reliability Engineering Statistics
    • Quality Engineering Statistics
    • An Introduction to Reliability Engineering
    • Reliability Engineering for Heavy Industry
    • An Introduction to Quality Engineering
    • Process Capability Analysis course
    • Root Cause Analysis and the 8D Corrective Action Process course
    • Return on Investment online course
    • CRE Preparation Online Course
    • Quondam Courses
  • Webinars
    • Upcoming Live Events
  • Calendar
    • Call for Papers Listing
    • Upcoming Webinars
    • Webinar Calendar
  • Login
    • Member Home

by Robert (Bob) J. Latino Leave a Comment

The 4 Physical Failure Mechanisms of Component Failure: The Basics (Part 1)

The 4 Physical Failure Mechanisms of Component Failure: The Basics (Part 1)

This article is directed at those ‘first responders’ who arrive immediately at the failure scene. These are the people who have to ensure the area is safe, preserve the scene for investigators and contribute to a plan to expedite a quick, safe return to production norms.

Many do not understand how valuable failed parts are to the metallurgical/forensic investigators. Broken parts are to metallurgists’, like the murder weapon is to a forensic crime investigator.

This article is meant to educate those that have access to the failed parts first, as to why they should preserve them in their failed state (not cleaning them up). We want to give them enough knowledge to be dangerous and raise their curiosity as to making a call on the fracture patterns they see.

Most all components fail for one, or a combination of, four (4) major physical reasons.

  1. Erosion
  2. Corrosion
  3. Fatigue
  4. Overload

In Part I of this mini-series, we will explore Erosion and Corrosion. We will save Fatigue and Overload for Part II (in an effort to make the learning more digestible in smaller chunks:-).

When investigating failures involving components, their fracture surfaces will tell a story as to what happened to them. As you approach any such failure scene, try and visualize being that failed part and thinking to yourself, “What just happened to me?” Visualize the part being in operation and the forces affecting it. Seems kind of corny, but it is a very effective approach to understanding of what happened. Let’s explore the basics of these very involved failure patterns.

Erosion

Erosion is caused by the presence of particles in the process medium contacting a surface and damaging it. Erosion can be delivered from fluid/air:

  • Fluid/air contaminated (particles present)
  • Fluid/air viscosity changed
  • Fluid/air velocity changed
  • Material eroding is wrong material for existing service
  • Materials are not compatible

Erosion can be abrasive or adhesive. Here are some basic examples:

Corrosion

Corrosion is the deterioration of a material due to interaction with its environment. It is the process in which metallic atoms leave the metal or form compounds in the presence of water and gases. Metal atoms are removed from a structural element until it fails, or oxides build up inside a pipe until it is plugged. Corrosion is an electro-chemical process. Corrosion can be complicated. To identify that there is corrosion should be sufficient for novices. Further detailed analysis should be performed by a qualified professional.

The are several types of corrosion, such as:

  • Uniform Attack
  • Pitting Corrosion Attack
  • Crevice Corrosion Attack
  • Galvanic Corrosion Attack
  • Erosion-Corrosion Attack
  • Stress Corrosion Cracking
  • Fretting Corrosion Attack

There are numerous variables that can create corrosion, here are some:

  • Contamination/impurities
  • Water quality
  • Aeration
  • Galvanic couples
  • Material selection
  • Effects of welding
  • Stagnation
  • Turbulence
  • Pressure
  • Deposits
  • Crevices
  • Startups and shutdowns

Here are some basic examples of each type of corrosion:

For the seasoned investigative veterans, this information will be old news (Investigation 101). However, the more the front-line folks in the field know these basics, the more they will be able to assist these veterans in their investigations. Proper investigations just cannot be comprehensive and thorough, without this physical evidence. So in the end, we are all helping out each other.

This will conclude Part I of our Component Failure Basics (2 of the 4 primary failure mechanisms). We will address the last ones (Fatigue and Overload) in Part II, in the coming weeks.

Filed Under: Articles, on Maintenance Reliability, The RCA

About Robert (Bob) J. Latino

Robert Latino is currently a Principal at Prelical Solutions, LLC, along with his brother Ken Latino.  Bob was a Founder and CEO of Reliability Center, Inc. (RCI), until it was acquired in 2019.  RCI is a 50-year-old Reliability Consulting firm specializing in improving Equipment, Process and Human Reliability. Mr. Latino received his Bachelor’s degree in Business Administration and Management from Virginia Commonwealth University. 

« The Problems with Payback Period, Part 1
5 Steps to Securing Commitment for a Transformer Reliability Program »

Leave a Reply Cancel reply

Your email address will not be published. Required fields are marked *

logo for The RCA article series image of BobArticle by Robert (Bob) J. Latino
CEO of Reliability Center, Inc.

in the The RCA article series

Join Accendo

Receive information and updates about articles and many other resources offered by Accendo Reliability by becoming a member.

It’s free and only takes a minute.

Join Today

Recent Posts

  • test
  • test
  • test
  • Your Most Important Business Equation
  • Your Suppliers Can Be a Risk to Your Project

© 2025 FMS Reliability · Privacy Policy · Terms of Service · Cookies Policy